Laser Welding of ARMOX 500T Steel

The article describes the results of the study on laser welding of armor plates with a nominal thickness of 3.0 mm. The plates were made of Armox 500T steel characterized by a hardness of up to 540 HB, a minimum yield strength of 1250 MPa, an ultimate strength of up to 1750 MPa, and an elongation A5 minimum of 8%. The laser used for the welding tests was a solid state Yb:YAG laser. The influence of basic parameters such as laser output power, welding speed, and focal plane position on the weld geometry was determined during bead-on-plate welding tests. The optimal conditions for butt joint welding were determined, and the test joints were subjected to mechanical and impact tests, metallographic analysis, and hardness measurements. It has been shown that it is possible to laser weld Armox 500T armor plates, and at the same time it is possible to provide high quality butt joints, but this requires precise selection of welding parameters. A decrease in HAZ hardness of about 22-35% in relation to the hardness of the base material, ranging from 470 to 510 HV0.2, was found. The ultimate tensile strength of the test joints was approx. 20% lower than the Armox 500T steel. The bending tests revealed the low plasticity of the tested joints because the bending angle was just 25-35°. The results of Charpy V-notch test revealed that the impact toughness of the weld metal at -20 °C was approx. 30% lower than at room temperature.