Stress-Corrosion-Cracking Sensitivity of the Sub-Zones in X80 Steel Welded Joints at Different Potentials

X80 steel plays a pivotal role in the development of oil and gas pipelines; however, its welded joints, particularly the heat-affected zone (HAZ), are susceptible to stress corrosion cracking (SCC) due to their complex microstructures. This study investigates the SCC initiation mechanisms of X80 steel welded joints under practical pipeline conditions with varying levels of cathodic protection. The SCC behaviors were analyzed through electrochemical measurements, hydrogen permeation tests, and interrupted slow strain rate tensile tests (SSRTs) conducted in a near-neutral pH environment under different potential conditions (OCP, -1.1 V_SCE, -1.2 V_SCE). These behaviors were influenced by microstructure type, grain size, martensite/austenite (M/A) constituents, and dislocation density. The sub-zones of the weld exhibited differing SCC resistance, with the fine-grain (FG) HAZ, base metal (zone), welded metal (WM) zone, and coarse-grain (CG) HAZ in descending order. In particular, the presence of coarse grains, low dislocation density, and extensive M/A islands collectively increased corrosion susceptibility and SCC sensitivity in the CGHAZ compared to other sub-zones. The SCC initiation mechanisms of the sub-zones within the X80-steel welded joint were primarily anodic dissolution (AD) under open-circuit potential (OCP) condition, shifting to either hydrogen-enhanced local plasticity (HELP) or hydrogen embrittlement (HE) mechanisms at -1.1 V_SCE or -1.2 V_SCE, respectively.