A Review of the Vaporization Behavior of Some Metal Elements in the LPBF Process

Metal additive manufacturing technology has developed by leaps and bounds in recent years; selective laser melting technology is a major form in metal additive manufacturing, and its application scenarios are numerous. For example, it is involved in many fields including aerospace field, automotive, mechanical processing, and the nuclear industry. At the same time, it also indirectly provides more raw materials for all walks of life in our country. However, during the selective laser melting process, due to the action of high-energy-density lasers, the temperature of most metal powders can reach above the vaporization temperature. Light metals with relatively low vaporization temperatures such as magnesium and zinc have more significant vaporization and other behaviors. At the same time, during the metal vaporization process, a variety of by-products are generated, which seriously affect the forming quality and mechanical properties of the workpiece, resulting in the workpiece quality possibly not reaching the expected target. This paper mainly interprets the metal vaporization behavior in the LPBF process and summarizes the international research progress and suppression methods for vaporization.