Preparation and Properties of Composite Double-Network Gel for Inhibiting Coal Spontaneous Combustion

In order to improve the inhibition effect of gel on coal spontaneous combustion, a chitosan (CS)/polyacrylamide (PAM)/metal ion (Al₃⁺) composite double-network gel was developed in this study. The optimum formula of the composite double-network gel was determined using orthogonal experimentation. The microstructure, water retention, compressibility, and anti-destruction properties of the composite double-network gel were analyzed. The inhibition effect of the composite double-network gel on coal spontaneous combustion was studied via infrared spectroscopy and a synchronous thermal analyzer from the micro and macro perspectives. The results show that the composite double-network gel has a denser interpenetrating double-network structure and a larger void ratio than the ordinary gel. The water retention rate was 55% after standing at 150 °C for 12 h. The deformation memory ratio of the composite double-network gel was 78%, which was 26.8% higher than that of the ordinary gel, and the compressive strength also increased by 59.96%. In addition, the critical temperature point and the maximum thermal weight-loss rate temperature point decreased by 7.01 °C and 39.62 °C, respectively, and the composite double-network gel effectively reduced active functional groups in the treated coal sample, such as hydroxyl and aliphatic hydrocarbons. In this study, a CS/PAM/Al₃⁺ composite double-network gel was produced, which exhibited good gel performance and inhibition effects, with physical effects such as the covering, wetting, and cementation of coal.