Zein-incorporated magnesium oxide nanoparticles (zMgO NPs) can influence the mechanical properties of dental materials. However, the effect of this addition on the mechanical properties of resin composite has yet to be investigated. The objective of this study was to add various concentrations of zMgO NPs to conventional, flowable, and bulk-fill composite and assess the effect on the compressive strength, flexural strength, and microhardness.

150 samples each of conventional composite, flowable composite, and bulk-fill composite (n = 450) were enhanced with concentrations of zMgO NPs at 0 %, 0.3 %, 0.5 %, 1 %, and 2 % (n = 30). 10 samples of each group were randomly allotted to the compressive strength, flexural strength, or hardness test. Characterization of the specimens was performed by X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and transmission electron microscopy. Two-way ANOVA test was used to compare between groups, and one-way ANOVA followed by Tukey's test was done at p = 0.05 to determine significance.

Characterization yielded a uniform distribution of nanoparticles in the matrix and the formation of a new hybrid composite that maintained its properties. Composite of all types enhanced with 0.3 % and 0.5 % zMgO NPs demonstrated a statistically significant increase in compressive strength, flexural strength, and hardness when compared to the control (p < 0.05). The bulk-fill composite with zMgO NPs concentrations of all groups demonstrated a statistically significant increase (p < 0.05) in hardness when compared to the control.

The modified composites' compressive strength, flexural strength, and hardness improved or remained consistent.

An improved dental resin composite will enhance the quality of care and patient experience. The augmented strength and hardness of resin composite is desirable in prolonging the durability of the restoration.