Engineering properties as a supplement cementitious material of ground copper reduction slag extracted valuable metal

Jin-Man Kim1, Sun-Mi Choi2, Sang-Chul Shin3

  • 1Department of Green Smart Architectural Engineering, Kongju National University, 1223-24, Cheonan-daero, Cheonan, Chungnam, Republic of Korea.

Heliyon
|July 29, 2024
PubMed

Keywords:
Copper reduction slagGrinding efficiencyHydrothermal conditionSupplementary cementitious materialsTobermorite

More Related Videos

Fabrication and Testing of Catalytic Aerogels Prepared Via Rapid Supercritical Extraction09:28

Fabrication and Testing of Catalytic Aerogels Prepared Via Rapid Supercritical Extraction

Published on: August 31, 2018

7.3K
An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature14:51

An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature

Published on: September 23, 2018

6.9K

Related Concept Videos

Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate...
100
Additives and Fillers in Concrete01:29

Additives and Fillers in Concrete

Additives and fillers are integral to enhancing the properties of concrete. Pozzolans and blast-furnace slag are additives or admixtures due to their reactions with calcium hydroxide released during cement hydration. Fillers, which are finely ground and similar in fineness to Portland cement, improve concrete attributes such as workability density, and reduce capillary bleeding or cracking. Some fillers possess hydraulic properties or participate in benign reactions within the cement paste.
The...
92
Ferrocement01:30

Ferrocement

Ferro-cement is a distinctive construction material that represents an innovative variant of reinforced concrete, characterized by its unique composition and the method by which it is formed. Unlike standard reinforced concrete, which relies on larger steel bars for reinforcement, ferro-cement utilizes densely packed layers of mesh or fine rods, fully encased in cement mortar. This composition allows for the creation of structures that are significantly thinner and more flexible than their...
160
Aggregate Cement Ratio01:21

Aggregate Cement Ratio

The Aggregate Cement ratio refers to the weight of aggregate divided by the weight of cement in a concrete mix. Altering this ratio has profound effects on the concrete's properties. This ratio plays a pivotal role in determining the strength, workability, and durability of concrete. When the Aggregate Cement ratio is higher, the mix is leaner, meaning it has less cement paste to lubricate the aggregate, potentially making the concrete less workable. Such mixes, known as lean, enhance the...
231
Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is...
107
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
106