Sulfoaluminate cement-modified loess as bioretention cell filler for nutrient removal from stormwater runoff

In order to reduce the consumption of sand and gravel resources, the use of loess can reduce transportation costs and realize the in-situ construction of spongy in areas with rich loess resources. But the collapsibility and low permeability of loess make it unable to be directly used as the filler of bioretention cells. In this study, sulfoaluminate cement (SAC) mixed with a small amount of basalt fiber was considered to be used for loess modification, and the physicochemical properties and nutrient removal effect of SAC-modified loess as filler in bioretention cells were comprehensively evaluated. The results showed that when the SAC dosage was 15% and the basalt fiber addition was 0% (S15B0) and 0.6% (S15B6) and the curing time was 14 days, the stability and appropriate permeability can be exhibited, which can preliminarily satisfy the requirements of bioretention cell. SAC made the maximum adsorption capacity of S15B0 and S15B6 for ammonia nitrogen (NH₄⁺-N) and phosphate higher than that of sand by 10.96%-31.51% and 45.92%-76.72%, respectively. The hydration products in SAC modified loess can fill the internal pores of loess particles and provide structural support, and ultimately reduce the accumulated pores, mesoporous pore size (20%) and surface homogeneity. Both S15B0 and S15B6 showed good removal effects of NH₄⁺-N and COD. The TP removal efficiency was stable at 95.43%∼99.95%. Both the antecedent drying days and the submerged zone have an effect on the nitrogen removal in the bioretention cells, where a longer antecedent drying days is detrimental to the nitrogen removal, and the installation of a submerged zone improves the nitrogen removal. The basalt fiber can enhance the transformation process from nitrate-nitrogen to nitrite-nitrogen in the bioretention cell. Therefore, the modification of SAC can provide a certain idea for the in-situ use of loess as the filler of the bioretention cell.