Eco-friendly, highly interpenetrated and slightly swollen pHEMA hydrogel foam for durable underwater...

Despite the emergence of hydrogels as ideal candidates for preparing the superhydrophilic materials for emulsion separation, their structural stability and swelling still hinder their long-term use, mainly due to structure defects after swelling. Herein, differing from the common modification, the eco-friendly poly 2-hydroxyethyl methacrylate (pHEMA) hydrogel foam was designed and synthesized via a one-step strategy by using the high internal phase emulsion (HIPE) template method, which endowed it with a highly interpenetrated porous structure. Unlike the normal swellable hydrogels such as poly(N-isoproplyacrylamide) (PNIPAM) hydrogel, or modified hydrogel coatings, the pHEMA hydrogel foam displayed stable structure and underwater superoleophobicity after 20 d of immersion in water. The pHEMA hydrogel foam could separate different kinds of highly surfactant-stabilized oil-in-water (O/W) emulsions with a high separation efficiency of 99.3% for liquid paraffin emulsion obtained solely under gravity-driven. Additionally, it exhibited excellent antifouling performance and long-term acid/alkali tolerance over 100 h without decrease in emulsion separation efficiency (98.0%, oil/water ratio of 99:1) and permeation flux (over 2000 L·m^-2·h^-1) attributed to its stable bulky structure. Moreover, the pHEMA hydrogel foam demonstrated high cell viability of 96.87% and 95.96% after culturing the 3T3 clone A31 cells in the pHEMA hydrogel foam for 24 h and 48 h, respectively, indicating good biocompatibility. Hence, our work provides a new design to develop an eco-friendly bulk hydrogel foam that achieves stable structure and performance for emulsion separation.