Bis-EMA/Bis-GMA ratio effects on resin-properties and impregnated fiber-bundles
Muhanad M Hatamleh1, Adilson Yoshio Furuse2
1Department of Applied Dental Sciences, Faculty of Applied Medical Sciences, Jordan University of Science and Technology, PO Box 3030, Irbid 22110, Jordan.
Objectives:
To evaluate the effect of different ratios of Bis-EMA/Bis-GMA resin mixtures on the inherent viscosity and curing-related properties: including degree of cure (DC%), shrinkage strain, Knoop micro-hardness (KH) and flexural strength of resin-impregnated fiber-bundles.
Methods:
Bis-EMA/Bis-GMA monomers were mixed (by weight) in the following ratios: M1 = 30 %/70 %, M2 = 50 %/50 %, M3 = 70 %/30 %, and M4 = 100 %/0 %. Standard measurements were made of refractive index, viscosity, degree of conversion, shrinkage strain and Knoop hardness (KHN). For 60 % glass fiber-bundles impregnated with 40 % resin, three-point bending test for flexural strength and shrinkage strain were measured. Data were analyzed by One-way ANOVA and Bonferroni post-hoc tests (α = 0.05).
Results:
For resin mixtures, increasing Bis-EMA proportion decreased refractive index (p < 0.05), and viscosity (p < 0.05), and increased monomer conversion (DC%), shrinkage strain and KHN (p < 0.05). DC% increased after 1 h for all resin mixtures. The shrinkage strain and flexural strength of resin-impregnated fiber-bundles reduced with increased Bis-EMA.
Significance:
Monomeric mixtures with highest amounts of Bis-EMA showed enhancement in several clinically-relevant properties and polymerization of respective resin-impregnated glass fibers. This makes them potential candidates for impregnating glass fibers in fiber-reinforced restorations.