Thermoresponsive On-Demand Adhesion and Detachment of a Polyurethane-Urea Bioadhesive

The development of bioadhesives with strong adhesion and on-demand adhesion-detachment behavior is still critically important and challenging for facilitating painless and damage-free removal in clinical applications. In this work, for the first time, we report the easy fabrication of novel polyurethane-urea (PUU)-based bioadhesives with thermoresponsive on-demand adhesion and detachment behavior. The PUU copolymer was synthesized by a simple copolymerization of low-molecular-weight, hydrophilic, and biocompatible poly(ethylene glycol), glyceryl monolaurate (GML, a special chain extender with a long side hydrophobic alkyl group), and isophorone diisocyanate (IPDI). Here, GML was expected to not only adjust the temperature-dependent adhesion behavior but also act as an internal plasticizer. By simple adjustment of the water content, the adhesion strength of the 15 wt % water-containing PUU film toward porcine skin is as high as 55 kPa with an adhesion energy of 128 J/m² at 37 °C. The adhesion strength dramatically decreases to only 3 kPa at 10 °C, exhibiting switching efficiency as high as 0.95. Furthermore, the present PUU-based adhesive also shows good on-demand underwater adhesion and detachment with a cell viability close to 100%. We propose that biomaterial research fields, especially novel PUU/polyurethane (PU)-based functional materials and bioadhesives, could benefit from such a novel thermoresponsive copolymer with outstanding mechanical and functional performances and an easy synthesis and scaled-up process as described in this article.