Rapid Synthesis of Ruthenium-Copper Nanocomposites as High-Performance Bifunctional Electrocatalysts for...

Development of high-performance, low-cost catalysts for electrochemical water splitting is key to sustainable hydrogen production. Herein, ultrafast synthesis of carbon-supported ruthenium-copper (RuCu/C) nanocomposites is reported by magnetic induction heating, where the rapid Joule's heating of RuCl₃ and CuCl₂ at 200 A for 10 s produces Ru-Cl residues-decorated Ru nanocrystals dispersed on a CuCl_x scaffold, featuring effective Ru to Cu charge transfer. Among the series, the RuCu/C-3 sample exhibits the best activity in 1 m KOH toward both the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER), with an overpotential of only -23 and +270 mV to reach 10 mA cm^-2, respectively. When RuCu/C-3 is used as bifunctional catalysts for electrochemical water splitting, a low cell voltage of 1.53 V is needed to produce 10 mA cm^-2, markedly better than that with a mixture of commercial Pt/C+RuO₂ (1.59 V). In situ X-ray absorption spectroscopy measurements show that the bifunctional activity is due to reduction of the Ru-Cl residues at low electrode potentials that enriches metallic Ru and oxidation at high electrode potentials that facilitates the formation of amorphous RuO_x. These findings highlight the unique potential of MIH in the ultrafast synthesis of high-performance catalysts for electrochemical water splitting.