Energetic silicones: synthesis and characterization of pentaoxadiazole-PDMS copolymers

Copolymers are the products obtained from the polymerization of multiple monomer species. So, in a polymer chain itself, there can be multiple repeating units that come from different monomers. The process of synthesizing a polymer from different monomer species is called copolymerization. When two monomers are involved, the polymer is known as a bipolymer. Polymers with three and four monomers are termed terpolymers and quaterpolymers, respectively. Figure 1 depicts the copolymerization of...

Acyclic diene metathesis polymerization or ADMET polymerization involves cross-metathesis of terminal dienes, such as 1,8-nonadiene, to give linear unsaturated polymer and ethylene. As ADMET is a reversible process, the formed ethylene gas must be removed from the reaction mixture to complete the polymerization process.
Similar to cross-metathesis, ADMET also involves the formation of metallacyclobutane intermediate by [2+2] cycloaddition of one of the double bonds of a terminal diene with...

Recently, the development of olefin metathesis polymerization advanced the field of polymer synthesis. Simply put, the reorganization of substituents on their double bonds between two olefins in the presence of a catalyst is known as the olefin metathesis reaction. The use of metathesis reaction for polymer synthesis is called olefin metathesis polymerization.
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists...

Ring-opening metathesis polymerization or ROMP involves strained cycloalkenes as starting materials. The mechanism of ROMP proceeds by reacting cycloalkene with Grubbs catalyst to give metallacyclobutane intermediate which undergoes a ring-opening reaction to form new carbene. The new carbene reacts with another molecule of cycloalkene. Repetition of these steps leads to the formation of an unsaturated open-chain polymer product. All these steps are reversible, however, relieving the ring...

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...