Fatigue Strength Improvement of Laser-Directed Energy Deposition 316L Stainless Steel with In Situ Ultrasonic Rolling...

In this study, to improve the fatigue strength of the LDED (laser-directed energy deposition) 316L stainless steel, an in situ ultrasonic rolling technology is developed to assist the laser-directed energy deposition process (LDED-UR). The microstructural characteristics and fatigue behavior are comprehensively discussed. The results show that the average size of pores of the LDED-UR alloy is about 10.2 μm, which is much smaller than that of the LDED alloy (34.1 μm). Meanwhile, the density of the LDED alloy is also enhanced from 98.26% to 99.27% via the in situ ultrasonic rolling. With the application of the in situ ultrasonic rolling, the grains are transformed into fully equiaxed grains, and their average grain size is greatly reduced from 84.56 μm to 26.93 μm. The fatigue limit of the LDED-UR alloy is increased by 29% from 210 MPa (LDED alloy) to 270 MPa, which can be ascribed to the decreased porosity and the fine grains. In particular, the crack initiation site of the LDED alloy is located at the surfaces, while it is nucleated from the sub-surface for the LDED-UR alloy. This is mainly attributed to the compression residual stress induced by the in situ ultrasonic rolling. This research offers a valuable understanding of the failure mechanisms in additively manufactured metals, guiding the development of effective strategies to improve their fatigue threshold under severe operating conditions.