Enhancement of chitosan-based film physicochemical and storage properties by interaction with proanthocyanidin and...

Deep eutectic solvent (DES) has been recognized as a promising plasticizer for the preparation of biodegradable food packaging films. In addition, DES-plasticized chitosan (CS) films could also serve as a favorable carrier for loading active components. In this work, a ternary composite film was fabricated by plasticizing chitosan with DES and the active ingredient proanthocyanidin (PA) was used as a cross-linking agent. The incorporation of PAs significantly enhanced the toughness, elasticity, and hydrophobicity of the ternary CS-DES-PA composite films. It achieved antioxidant and bacteriostatic functions. In particular, the ternary CS-DES-PA composite films had a thickness of 0.16 ± 0.01 μm, a tensile strength of 2.63 ± 0.48 MPa, and an elongation about 73.22 %. They also have improved water resistance, UV blocking, with a high-water contact angle of 88.4° and a low water swelling of 5 % on the surface of the film. Meanwhile, the PAs in the film could slow down the browning of litchi fruits. This ternary blended film (CS-DES-PA) achieves better compatibility of the active ingredient in the film-forming substrate. It also provides a green and biodegradable packaging material for food packaging.