Sonochemical deposition of gold nano-shells on suspended polymeric spheres

Metal nanoparticles have drawn great interest due to their unique properties for applications in the fields of catalysis, biomedicine and environmental science depending on the architecture of the metal nanoparticle composites. Amongst different designing routes, the chemical template deposition offers great flexibility in terms of the template selection and interfacial interactions, giving rise to controllable designs. In order to control over nanoparticle size distribution and deposition efficiency, a sonochemical approach has been systematically followed in this study. Key parameters of the ultrasound-assisted deposition procedures during the seeding step to synthesise gold nanoparticle-coated poly(styrene) beads were investigated. The impact of the solution pH and the ultrasonic frequency on the template deposition was examined at 139, 300, 500 and 1000 kHz. The results, monitored by transmission electron spectroscopic imaging, show that the highest gold deposition was achieved at 300 kHz, revealing the mechanistic details of the nucleation-crystal growth behaviour as a function of ultrasonic frequency and reaction time. In addition, the concentration ratio between gold ions and poly(styrene) beads was varied. The highest deposition coverage and smallest particle size were reached at 0.05 mM and 2.5 mg, respectively. The proposed mechanism of the MNPs formation and deposition behaviour were then discussed based on the tested parameters.