Accelerated aging behavior of degradable and non-degradable microplastics via advanced oxidation and their adsorption characteristics towards tetracycline

The increasing global utilization of biodegradable plastics due to stringent regulations on traditional plastics has caused a significant rise in microplastic (MPs) pollution in aquatic ecosystems from biodegradable products. However, the environmental behavior of biodegradable MPs remains inadequately elucidated. This study explored the aging processes of polylactic acid (PLA) and polystyrene (PS) under a heat-activated potassium persulfate (K₂S₂O₈) system, as well as their adsorption characteristics towards tetracycline (TCs). In comparison to PS, the surface structure of PLA experienced more pronounced changes over aging, exhibiting evident pits, cracks, and fragmentation. The carbonyl index (CI) and oxygen/carbon ratio (O/C) of PS displayed exponential growth over time, whereas the values for PLA showed linear and exponential increases, respectively. The adsorption capacity of TCs by PS and PLA aged for 6 days increased from 0.312 mg‧g^-1 and 0.457 mg‧g^-1for original PS and PLA, respectively, to 0.372 mg‧g^-1 and 0.649 mg‧g^-1. Meanwhile, the adsorption rate (k₂ values) for TCs decreased by 42.03 % for PS and 79.64 % for PLA compared to their initial values. The findings indicated that biodegradable PLA-MPs may exhibit higher tetracycline carrying capacities than PS, potentially increasing environmental and organismal risks, particularly in view of aging effects.