A promising poly (e-caprolactone)/graphene-based scaffold as an antibacterial in regenerating bone tissue

Scaffolds are 3D biomaterials that provide an environment for cell regeneration. In the context of bone remodeling, poly(e-caprolactone) (PCL) combined with graphene has been developed as the scaffold. It is imperative for scaffolds to possess antibacterial properties in order to properly reduce the risk of potential infections.Therefore, this study aims to analyze the antibacterial characteristics of PCL/graphene scaffolds against Staphylococcus aureus (S. aureus) and Porphyromonas gingivalis (P. gingivalis) in vitro. In this study, five different groups were used, including PCL (K-), Amoxicillin (K+), PCL/Graphene 0.5 wt%, PCL/graphene 1 wt% and PCL/Graphene 1.5 wt%. All experiments were performed in triplicates and were repeated three times, and the diffusion method by Kirby-Bauer test was used. The disc was incubated with S. aureus and P. gingivalis for 24 hours and then the diameter of the inhibition zone was measured. The results showed that the PCL/graphene scaffolds exhibited dose-dependent antibacterial activity against S. aureus and P. gingivalis. The inhibition zone diameter (IZD) against S. aureus of PCL/graphene 1 wt% was 9.53 ± 0.74 mm, and increased to 11.93 ± 0.92 mm at a concentration of 1.5 wt% of graphene. The PCL/graphene scaffold with 1.5 wt% exhibited a greater inhibitory effect, with an IZD of 12.56 ± 0.06 mm against P. gingivalis, while the inhibitory activity of the 1 wt% variant was relatively lower at 10.46 ± 0.24 mm. The negative control, PCL, and PCL/graphene 0.5 wt% exhibited no antibacterial activity sequentially (p = 1). Scaffolds of poly(e-caprolactone)/graphene exhibited an antibacterial activity at 1, and 1.5 wt% on S. aureus and P. gingivalis. The antibacterial properties of this scaffold make it a promising candidate for regenerating bone tissue.