Adsorption behavior of heavy metals onto microplastics derived from conventional and biodegradable commercial plastic...

This study extensively explored the adsorption behavior of heavy metals (Pb⁺², Ni⁺², Cu⁺², Zn⁺², and Cd⁺²) onto microplastics (MPs). The particle sizes of MPs ranged from 0.149 to 0.25 mm. The microplastics were generated from commercial products manufactured from both conventional (polyethylene (PE) bottle, polystyrene (PS) spoon, and polyethylene terephthalate (PET) egg carton) and biodegradable (polylactic acid (PLA) spoon, and polylactic acid (PLA) egg carton) plastics. The study also considered the influence of solution pH on the adsorption capacity of heavy metals. Regarding the adsorption potential for Cu⁺², the ranking was as follows: PLA-egg (1408 μg·g^-1) > PLA-spoon (735 μg·g^-1) > PE-bottle (315 μg·g^-1) > PET-egg (283 μg·g^-1) > PS-spoon (237 μg·g^-1). PLA MPs showed the highest adsorption capacity due to the lower thermal stability and higher presence of surface oxygen functional groups. Moreover, the adsorption capacities of the five metals onto PLA-spoon and PLA-egg decreased in the following order: Pb (1785 μg·g^-1) > Zn (1267 μg·g^-1) > Cd (748 μg·g^-1) > Cu (735 μg·g^-1) > Ni (722 μg·g^-1), and Pb (1520 μg·g^-1) > Ni (1412 μg·g^-1) > Cu (1408 μg·g^-1) > Zn (1118 μg·g^-1) > Cd (423 μg·g^-1), respectively. The SEM-EDS, FTIR and XPS results demonstrated that surface oxygen-containing functional groups play an important role during the adsorption process. This study extended its analysis to quantify the metal content of the post-adsorption MPs, revealing uneven adsorption of heavy metals onto the MPs. This implies that the diversity of commercial plastic products may result in significant variations in their ability to adsorb heavy metals, underscoring the importance of effectively managing discarded commercial plastic products.