Low temperature carbonization and synergistic flame retardancy of cotton fabric coated by phosphorus‑nitrogen flame...

To solve the problems of flammability and smoldering of cotton fabric, its flame-retardant finishing was executed with biomass wool keratin (WK) and cyclic phosphate ester (CPE) through the soaking and baking process. The synergistic mechanism of WK low-temperature melting and CPE catalytic dehydration prompted the formation of protective carbonization layer on cotton fabric surface, and this protective layer reduced its pyrolysis rate, inhibited the production of combustible materials and improved its flame retardancy. The results of synchronous thermal analysis indicate that the initial decomposition temperature of WK and CPE is lower than that of cotton fabric, and they precede the endothermic degradation before fabric main body. This effectively promotes the low-temperature carbonization of cotton fabric and inhibits its pyrolysis. The initial decomposition temperature of WK/CPE treated fabrics advances by 47.9 °C-97.8 °C, presenting significant low-temperature carbonization trend. Moreover, they form 3.0 %-20.0 % aromatic structural char before the pyrolysis of cotton cellulose due to the low-temperature dehydration and carbonization reactions. The damage length after vertical burning is only 4.0 cm for treated fabric with five layers, its after-flame and smoldering disappear, and its limiting oxygen index value increases to 28.7 %. This research provides an effective idea for the flammability and smoldering problems of cotton fabric.