A comparative study of PMMA/PEG polymer nanocomposites doped with different oxides nanoparticles for potential
Omar Abdel Salam1, Hisham A Hamad1, Mostafa A R Eltokhy1
1Electronic Technology Department, Faculty of Technology and Education, Helwan University, Saray-El Qoupa, El Sawah Street, Cairo, 11281, Egypt.
Abstract:
PMMA/PEG and PMMA/PEG doped with SiO2, TiO2, and Al2O3 were fabricated using the solution-casting technique. The composites were characterized by X-ray diffraction and scanning electron microscopy (FE-SEM), which revealed that the amorphous nature of PMMA/PEG blend doped with Al2O3 was hindered by the crystalline nature of those doped with SiO2 and TiO2. The absorption of PMMA/PEG blend doped with Al2O3 is higher, band gap energies were decreased from 4.90 eV for PMMA/PEG blend to 4.03 eV, 3.09 eV, and 2.09 eV for SiO2, TiO2, and Al2O3 doped PMMA/PEG blend, respectively. The dielectric constant, ε' has a high value (2 × 104) for samples PMMA/PEG and SiO2/PMMA/PEG. While dielectric loss -values decreased to < 100 for TiO2/PMMA/PEG and Al2O3/PMMA/PEG. Further, the fabricated composite SiO2/PMMA/PEG led to improvement the optical and dielectric properties compared with PMMA/PEG for optoelectronic such as manufacturing of optical fiber cables application. The results show TiO2/PMMA/PEG and Al2O3/PMMA/PEG are multifunctional can be used as low-permittivity nanodielectric and substrates to design the next generation of flexible electronic devices.