Effect of Bleaching Treatments on the Mechanical Properties of the Dentin Matrix and on Collagen Biodegradation by...

This study evaluated the mechanical properties of demineralized dentin matrix submitted to different bleaching treatments, as well as the changes in mass and collagen biodegradation brought about by endogenous protease. Dentin collagen matrices were prepared to receive the following treatments (n=12): no bleaching treatment (C-control), 10% carbamide peroxide (CP-Opalescence PF, Ultradent, South Jordan, UT, USA) 10%/8 hours/ day/14 days, and 40% hydrogen peroxide (HP-Opalescence Boost, Ultradent), 40 minutes per session/3 sessions. The dentin matrices were evaluated for elastic modulus and mass before and after treatments and ultimate tensile strength after treatments. The solution collected during storage was evaluated for hydroxyproline release. There was no statistically significant difference between CP and C in terms of the elastic modulus (p=0.3697) or mass variation (p=0.1333). Dentin beams treated with HP and C presented significant mass loss after the first session (p=0.0003). HP treatment led to complete degradation of collagen matrices after the second bleaching session. After the second session, CP showed higher hydroxyproline concentration than C (p<0.0001). Ultimate tensile strength was lower for CP than C (p=0.0097). CP did not affect the elastic modulus or the dentin collagen matrix mass but did promote hydroxyproline release by endogenous protease and reduce the ultimate tensile strength. HP significantly affected the mechanical properties of dentin and promoted complete degradation of the demineralized dentin collagen matrix.