Modified Hybrid Hydroxyapatite-Silver Nanoparticles Activated via a Blue Light Source in Various Concentrations in
Faisal Ali Bin Abbooud AlQhtani1, Muhammad Abdullah Kamran2, Shan Sainudeen3
1Consultant in Pediatric Dentistry, Department of Pediatric Dentistry and Orthodontic Sciences, College of Dentistry, King Khalid University, Abha, Saudi Arabia.
Abstract:
To evaluate hydroxyapatite-silver (HA-Ag) hybrid nanoparticles (NPs), as an antibacterial agent when integrated in self-etch (SE) adhesive. Blue light activated HA-Ag hybrid NP incorporation on mechanical properties, degree of conversion (DC), and microtensile bond strength (μTBS). Eighty primary molar teeth have carious lesions reaching the dentin but not involving the pulp. The infected dentin was removed and carious-affected dentin (CAD) was preserved. Forty samples were inoculated with Streptococcus mutans. All primary teeth (n = 80) were allocated into four groups based on the incorporation of HA-Ag hybrid NPs in different concentrations (0%, 1%, 5%, and 10%). Group 1: 0% HA-Ag hybrid NPs + Clearfil SE bond primer, group 2: 1% HA-Ag hybrid NPs + Clearfil SE bond primer, group 3: 5 wt% HA-Ag NPs + Clearfil SE bond primer, and group 4: 10 wt% HA-Ag NPs + Clearfil SE bond primer. The survival rate assessment of S. mutans was conducted on 40 inoculated samples. On the remaining primary teeth (n = 40), Clearfil SE bonding agent was applied uniformly via a blue light source. The composite buildup was performed on the samples and μTBS and failure analysis assessed. Fourier transform infrared spectroscopy was performed to assess DC. Survival rates of S. mutans and μTBS among the tested groups were compared using ANOVA and Tukey post hoc analysis. 10 wt % HA-Ag NPs + Clearfil SE bond primer exhibited the highest level of antibacterial efficacy (0.14 ± 0.02 CFU/mL) against S. mutans. The highest μTBS (18.38 ± 0.78 MPa) at the composite/CAD interface was in group 2 (1 wt % HA-Ag NPs + Clearfil SE bond primer + Clearfil SE bonding agent + activation with a blue light source). The highest DC was observed in the control group with Clearfil SE bond primer + Clearfil SE bonding agent + activation with a blue light source. 1 wt% HA-Ag hybrid NPs showed enhanced antibacterial effectiveness, DC, and bond strength of the SE adhesive to the primary CAD.