Yttrium doping stabilizes the structure of Ni3(NO3)2(OH)4 cathodes for application in advanced Ni-Zn batteries
Xinyu Feng1, Siwen Zhang1, Jiazhuo Li1
1Institute of Clean Energy Chemistry, Key Laboratory for Green Synthesis and Preparative Chemistry of Advanced Materials of Liaoning Province, College of Chemistry, Liaoning University, Shenyang 110036, China. yinbosi@lnu.edu.cn.
Abstract:
Ni3(NO3)2(OH)4 has a high theoretical specific capacitance, low cost, and environmental friendliness, making it a promising electrode material. Specifically, Ni3(NO3)2(OH)4 electrodes have a larger layer spacing (c = 6.898 Å) than Ni(OH)2 electrodes since NO3- has a much larger ionic radius than OH-. The larger layer spacing stores more electrolyte ions, significantly improving the electrochemical activity of the electrodes. Additionally, the interlayer NO3- can enhance the structural stability of Ni3(NO3)2(OH)4. However, since Ni3(NO3)2(OH)4 has a higher molar mass than Ni(OH)2, it has a lower theoretical specific capacity. Consequently, Ni3(NO3)2(OH)4 has not been used in zinc-based alkaline batteries. Studies showed that doping could enhance the electrochemical performance of electrode materials. Therefore, this study used a simple solvothermal reaction to synthesize yttrium-doped Ni3(NO3)2(OH)4 (Y-Ni3(NO3)2(OH)4), assembling a Y-Ni3(NO3)2(OH)4//Zn battery for electrochemical testing. Y-Ni3(NO3)2(OH)4 served as the cathode in the battery. The analysis of Y-Ni3(NO3)2(OH)4 showed that yttrium (Y) doping increased the specific surface area and pore size of Ni3(NO3)2(OH)4 significantly. The increased specific surface area improved the active material utilization, and the abundant mesopores facilitated OH- transport, substantially enhancing the battery's specific capacity and energy density. Ultimately, the specific discharge capacity of the advanced Y-Ni3(NO3)2(OH)4//Zn battery reached 177.97 mA h g-1 at a current density of 4 A g-1, nearly doubling the capacity of the earlier Ni3(NO3)2(OH)4//Zn battery (103.59 mA h g-1).
Related Concept Videos
02:48Ionic Bonding and Electron Transfer
02:46Crystal Field Theory - Tetrahedral and Square Planar Complexes
Crystal field theory (CFT) is applicable to molecules in geometries other than octahedral. In octahedral complexes, the lobes of the dx2−y2 and dz2 orbitals point directly at the ligands. For tetrahedral complexes, the d orbitals remain in place, but with only four ligands located between the axes. None of the orbitals points directly at the tetrahedral ligands. However, the dx2−y2 and dz2 orbitals (along the Cartesian axes) overlap with the ligands less than the dxy,...
03:45Formation of Complex Ions
01:09Complexation Equilibria: Factors Influencing Stability of Complexes
02:58Properties of Transition Metals
02:42Ionic Crystal Structures
Most monatomic ions behave as charged spheres, and their attraction for ions of opposite charge is the same in every direction. Consequently, stable structures for ionic compounds result (1) when ions of one charge are surrounded by as many ions as possible of the opposite...