Synthesis and Performance Evaluation of High-Temperature-Resistant Extreme-Pressure Lubricants for a Water-Based...

Addressing the high friction and torque challenges encountered in drilling processes for high-displacement wells, horizontal wells, and directional wells, we successfully synthesized OAG, a high-temperature and high-salinity drilling fluid lubricant, using materials such as oleic acid and glycerol. OAG was characterized through Fourier-transform infrared (FTIR) spectroscopy and thermogravimetric analysis (TGA). The research findings demonstrate the excellent lubricating performance of OAG under high-temperature and high-salinity conditions. After adding 1.0% OAG to a 4% freshwater-based slurry, the adhesion coefficient of the mud cake decreased to 0.0437, and at a dosage of 1.5%, the lubrication coefficient was 0.032, resulting in a reduction rate of 94.1% in the lubrication coefficient. After heating at 200 °C for 16 h, the reduction rate of the lubrication coefficient reached 93.6%. Even under 35% NaCl conditions, the reduction rate of the lubrication coefficient remained at 80.3%, indicating excellent lubrication retention performance. The lubricant OAG exhibits good compatibility with high-density drilling fluid gel systems, maintaining their rheological properties after heating at 200 °C and reducing filtration loss. The lubrication mechanism analysis indicates that OAG can effectively adsorb onto the surface of N80 steel sheets. The contact angle of the steel sheets increased from 41.9° to 83.3° before and after hot rolling, indicating a significant enhancement in hydrophobicity. This enhancement is primarily attributed to the formation of an extreme-pressure lubricating film through chemical reactions of OAG on the metal surface. Consequently, this film markedly reduces the friction between the drilling tools and the wellbore rocks, thereby enhancing lubrication performance and providing valuable guidance for constructing high-density water-based drilling fluid gel systems.