Experimental Characterization of Anisotropic Mechanical Behaviour and Failure Mechanisms of Hardened Printed Concrete

Extrusion-based printing of cementitious materials represents an innovative technology in civil engineering. The additive manufacturing process significantly influences the material properties in the hardened state, leading to anisotropic behaviour in terms of stiffness and strength compared to conventionally cast concrete. This experimental study aims to deepen the understanding of the mechanical behaviour of hardened printed concrete. Beam-like specimens with varying printing patterns, loading orientations and lengths are investigated within three-point bending tests (3PBT) and uniaxial compression tests (UCT). Homogenized material parameters such as Young's modulus, compressive and flexural tensile strength and density are statistically evaluated using optically measured displacement and strain fields on the specimen surface. The qualitative and quantitative results demonstrate a strong dependency of material properties and failure mechanisms on the printing pattern. The interfilamental and interlayer areas with weak adhesion are identified as the main reason for anisotropy.