Design and Microwave Absorption Performance Study of SiC-Fe₃O₄ Emulsified Asphalt Mixture

To address the challenges of slow curing speed and suboptimal microwave absorption during the paving of cold-mixed and cold-laid asphalt mixtures, this study introduces SiC-Fe₃O₄ composite material (SF) into emulsified asphalt mixtures to enhance microwave absorption and accelerate curing via microwave heating. Initially, based on the maximum density curve theory, an appropriate mineral aggregate gradation was designed, and the optimal ratio of emulsified asphalt mixture was determined through mixing tests, cohesion tests, wet wheel wear tests, and load wheel sand adhesion tests. Subsequently, the influence of SF content on the mixing performance of emulsified asphalt mixtures was analyzed through mixing and consistency tests. Finally, the microwave absorption performance of the mixture was evaluated by designing microwave heating tests under different conditions, using temperature indicators and quality indicators. The experimental results indicate that when SF content ranges from 0% to 4%, the mixing performance of the emulsified asphalt mixture meets specification requirements. The dosage of SF, SF composite ratio, and microwave power significantly impact microwave absorption performance, whereas environmental temperature has a relatively minor effect. The optimal mix ratio for the emulsified asphalt mixture is mineral aggregate:modified emulsified asphalt:water:cement = 100:12.8:6:1. The ideal SF dosage is 4%, with an optimal SiC to Fe₃O₄ composite ratio of 1:1, and a suitable microwave power range of 600-1000 W.