The Contribution of Nano-Alumina to Ultra-High-Performance Cement-Based Systems

In the last decades, nano-silica (NS), nano-alumina (NA), and nano-calcium oxide (NC) particles have been incorporated into cementitious materials, and it seems that each one of them contributes uniquely to the materials' properties. This research explores the influence of each nanomaterial on the fresh properties of cement pastes and their compressive strength evolution over one year. Low proportions (1.5% by weight) of nanomaterials were added to cement pastes, and their fresh properties, such as heat of hydration and X-ray diffraction patterns in the first hours, were analyzed. The compressive strength and open porosity were also measured long-term. The acceleration of hydration heat in NA-cement pastes is linked to enhanced hydration product formation at early ages. Among the tested nanomaterials, NA increased compressive strength by 10% at later ages. Although the fresh properties of NC-cement pastes remained unaffected, their open porosity decreased by 54% at 28 days. In contrast, the increase in heat of hydration in NS-cement pastes did not result in significant strength improvement. Based on these findings, NA was selected for ultra-high-performance cement (UHPC)-based material use. Its incorporation not only preserved the ultra-high-performance (UHP) properties but also provided additional benefits such as an increase in compressive strength under a CO₂ atmosphere. Through detailed analysis, this research establishes that nano-alumina incorporation optimizes the microstructural development and compressive strength of ultra-high-performance cement-based systems, presenting a novel advancement in enhancing the mechanical properties and durability of these materials under various environmental conditions.