Degradation of Biodegradable Nonwoven Mulches in the Winter Period

An open field experiment from November 2022 to May 2023 in Croatia, which is characterized by a continental humid climate, evaluated nonwoven mulches made from viscose, jute, and hemp fibres blended with PLA fibres. The blends of viscose and jute fibres (90:10, 80:20, and 70:30 ratios) were produced using mechanical web formation on cards with needle punching for bonding webs. Additionally, hemp fibres were blended with PLA fibres in a ratio of 80:20. Winter conditions caused significant structural changes in the mulches, including shrinkage, increased mass per unit area, thickness, and reduced air permeability. The amount of PLA fibre in the nonwoven mulch blends significantly affected nonwoven fabric structure change during exposure to winter conditions. After 180 days, the breaking force of all mulches increased by 30% to 277%. The soil beneath jute and hemp mulches maintained higher temperatures and moisture levels compared to viscose mulches. Soil organic carbon content varied with fibre type and was higher under jute and hemp mulches. K₂O content was significantly higher in soils covered by mulches. All mulches effectively suppressed weeds. The experiment results showed that the newly produced nonwoven mulches could replace the conventional agro foil. Results also suggest that choosing biodegradable nonwoven mulches produced from fibres obtained from natural and renewable sources can influence soil fertility and the availability of nutrients, ultimately affecting plant growth and agricultural productivity.