Effects of size and shape of hole defects on mechanical properties of biphenylene: a molecular dynamics study

The distinctive multi-ring structure and remarkable electrical characteristics of biphenylene render it a material of considerable interest, notably for its prospective utilization as an anode material in lithium-ion batteries. However, understanding the mechanical traits of biphenylene is essential for its application, particularly due to the volumetric fluctuations resulting from lithium ion insertion and extraction during charging and discharging cycles. In this regard, this study investigates the performance of pristine biphenylene and materials embedded with various types of hole defects under uniaxial tension utilizing molecular dynamics simulations. Specifically, from the stress‒strain curves, we obtained key mechanical properties, including toughness, strength, Young's modulus and fracture strain. It was observed that various near-circular hole (including circular, square, hexagonal, and octagonal) defects result in remarkably similar properties. A more quantitative scaling analysis revealed that, in comparison with the exact shape of the defect, the area of the defect is more critical for determining the mechanical properties of biphenylene. Our finding might be beneficial to the defect engineering of two-dimensional materials.