In vivo biocompatibility of a new hydrophobic coated Al/Al2O3 nanowire surface on stents
Axel Rentzsch1, Eva Metz1, Ruben Mühl-Benninghaus2
1Clinic for Pediatric Cardiology, Saarland University Hospital, Homburg, Saar, Germany.
Background:
Intima proliferation and in-stent restenosis is a challenging situation in interventional treatment of small vessel obstruction. Al/Al2O3 nanowires have been shown to accelerate vascular endothelial cell proliferation and migration in vitro, while suppressing vascular smooth muscle cell growth. Moreover, surface modification of Al/Al2O3 nanowires with poly[bis(2,2,2-trifluoromethoxy)phosphazene (PTFEP) coating enables further advantages such as reduced platelet adhesion. Therefore, the study's goal was to compare the biocompatibility of novel Al/Al2O3 + PTFEP coated nanowire bare-metal stents to uncoated control stents in vivo using optical coherence tomography (OCT), quantitative angiography and histomorphometric assessment.
Methods:
15 Al/Al2O3 + PTFEP coated and 19 control stents were implanted in the cervical arteries of 9 Aachen minipigs. After 90 days, in-stent stenosis, thrombogenicity, and inflammatory response were assessed. Scanning electron microscopy was used to analyse the stent surface.
Results:
OCT analysis revealed that neointimal proliferation in Al/Al2O3 + PTFEP coated stents was significantly reduced compared to control stents. The neointimal area was 1.16 ± 0.77 mm2 in Al/Al2O3 + PTFEP coated stents vs. 1.98 ± 1.04 mm2 in control stents (p = 0.004), and the neointimal thickness was 0.28 ± 0.20 vs. 0.47 ± 0.10 (p = 0.003). Quantitative angiography showed a tendency to less neointimal growth in coated stents. Histomorphometry showed no significant difference between the two groups and revealed an apparent inflammatory reaction surrounding the stent struts.
Conclusions:
At long-term follow-up, Al/Al2O3 + PTFEP coated stents placed in peripheral arteries demonstrated good tolerance with no treatment-associated vascular obstruction and reduced in-stent restenosis in OCT. These preliminary in vivo findings indicate that Al/Al2O3 + PTFEP coated nanowire stents may have translational potential to be used for the prevention of in-stent restenosis.