High performances of cellulose nanocrystal based bicomponent supramolecular hydrogel lubricant

To improve the limitations of water-based lubricants, a novel cellulose nanocrystal based supramolecular hydrogel (CNC/x-DG/y) was prepared by mixing cellulose nanocrystal (CNC) and diglycerol (DG) into deionized water (DW). The hydrogel was characterized to determine its material ratio and gelation mechanism. When DW was fixed at 1 mL, CNC content should be no <2.4 wt% and DG content 0.1-1.3 mL. The gelification was driven by the multiple H-bond network between CNC and DG, which immobilized water molecules. The rheological performances, the anti-rust property and the volatilization behaviour of the hydrogel were further studied. The results showed that the hydrogel had satisfactory viscoelasticity, excellent thermal stability, strong creep recovery, high anti-rust performance and low volatilization rate, which were exactly its advantages for use as lubricant. A typical representative of the hydrogel, namely CNC/2.4-DG/0.1, was selected to evaluate the tribological performances, and the resulting worn surfaces were analyzed. CNC/2.4-DG/0.1 exhibited a lower friction coefficient of 0.059 and a smaller wear volume of 0.81 × 10^-3 mm³, compared to DW(1 mL) + CNC(2.4 wt%) and DW(1 mL) + DG(0.1 mL). The outstanding tribological performances of CNC/2.4-DG/0.1 were reasonably attributed to the synergistic mending effect of CNC and DG and the dissipative effect of H-bonds between the two.