Mechanism of Pressure-Modulated Self-Trapped Exciton Emission in Cs₂TeCl₆ Double Perovskite

Pressure-modulated self-trapped exciton (STE) emission mechanism in all-inorganic lead-free metal halide double perovskites characterized by large Stokes-shifted broadband emission, has attracted much attention across various fields such as optics, optoelectronics, and biomedical sciences. Here, by employing the all-inorganic lead-free metal halide double perovskite Cs₂TeCl₆ as a paradigm, the authors elucidate that the performance of STE emission can be modulated by pressure, attributable to the pressure-induced evolution of the electronic state (ES). Two ES transitions happen at pressures of 1.6 and 5.8 GPa, sequentially. The electronic behaviors of Cs₂TeCl₆ can be jointly modulated by both pressure and ES transitions. When the pressure reaches 1.6 GPa, the Huang-Rhys factor S, indicative of the strength of electron-phonon coupling, attains an optimum value of ≈12.0, correlating with the pressure-induced photoluminescence (PL) intensity of Cs₂TeCl₆ is 4.8-fold that of its PL intensity under ambient pressure. Through analyzing the pressure-dependent STE dynamic behavioral changes, the authors have revealed the microphysical mechanism underlying the pressure-modulated enhancement and quenching of STE emission in Cs₂TeCl₆.