Halloysite functionalized with dendritic moiety containing vitamin B1 hydrochloride as a bio-based catalyst for the...

Using halloysite clay and vitamin B1 hydrochloride, a novel acidic halloysite-dendrimer catalytic composite has been developed for conversion of fructose to 5-hydroxymthylfurfural. To grow the dendritic moiety on halloysite, it was first functionalized and then reacted with melamine, epichlorohydrin and vitamin B1 hydrochloride respectively. Then, the resulting composite was treated with ZnCl₂ to furnish Lewis acid sites. Use of vitamin B1 as the cationic moiety of ionic liquid obviated use of toxic chemicals and resulted in more environmentally friendly composite. Similarly, dendritic moiety of generation 2 was also grafted on halloysite and the activity of both catalysts for conversion of fructose to 5-hydroxymthylfurfural was investigated to disclose the role of dendrimer generation. For the best catalytic composite, the reaction variables were optimized via RSM and it was revealed that use of 0.035 g catalyst per 0.1 g fructose at 95 °C furnished HMF in 96% yield in 105 min. Turnover numbers (TONs) and frequencies (TOFs) were estimated to be 10,130 and 5788 h^-1, respectively. Kinetic studies also underlined that Ea was 22.85 kJ/mol. The thermodynamic parameters of $$ , $$ and $$ , were calculated to be 23 kJ/mol, - 129.2 J/mol and 72.14 kJ/mol, respectively. Notably, the catalyst exhibited good recyclability and hot filtration approved heterogeneous nature of catalysis.