Unlocking high-efficiency charge storage: Co-assembled nanoparticles of lignin and polyaniline molecules

Redox-active lignin rich in phenolic hydroxyl groups is an ingenious charge storage material. However, its insulating nature limits the storage/release of electrons and requires the construction of electron transfer channels within it. Herein, nanoparticles (PANI/DKL-NPs) are prepared by co-assembly via π-π interactions between conducting polyaniline (PANI) and demethylated Kraft lignin (DKL) molecules for the first time, and rapid electron transfer inside DKL is achieved. The co-assembled PANI/DKL-NPs consist of interpenetrating structures of PANI and DKL at the molecular scale, and the content of PANI molecules interspersed within them is controllable. Meanwhile, the extensive and abundant mesoporous structure in nanoscale PANI/DKL-NPs facilitates ion transport and electron storage. Based on this favorable microstructure, the specific capacitance of PANI/DKL-NPs at 1 A·g^-1 is as high as 532 F·g^-1, which is 780 % and 90.68 % higher compared to DKL-NPs and PANI-NPs, respectively. Meanwhile, the rate performance of PANI/DKL-NPs is significantly enhanced than that of DKL-NPs (33.11 %) and comparable to that of PANI-NPs (more than 69 %). Furthermore, the symmetric supercapacitor (PANI/DKL-NPs//PANI/DKL-NPs) assembled from it achieves a high energy density of 27.49 Wh·kg^-1 at 400 W·kg^-1 power density, and superb flexibility and mechanical stability. Therefore, the co-assembly of DKL and PANI will effectively stimulate the energy storage potential of lignin, providing a practical pathway to promote the development of biopolymers in energy storage.