Fabrication of Mechanically Tunable and Bioactive Metal Scaffolds for Biomedical Applications
Published on: December 8, 2015
Long-term follow-up of bone density changes in total hip arthroplasty: comparative analysis from a randomized
Michael Axenhus1, Mats Salemyr2, Sebastian Mukka3
1Division of Orthopaedics, Department of Clinical Sciences at Danderyd Hospital, Karolinska Institutet, Entrévägen 2, 182 88, Danderyd, Stockholm, Sweden. michael.axenhus@ki.se.
Purpose:
Periacetabular bone loss poses a considerable challenge in the longevity and stability of acetabular implants used in total hip arthroplasty (THA). Innovations in implant design, specifically the introduction of three-dimensional (3D) porous titanium constructs, might reduce bone resorption. The purpose of this study was to build upon our previous randomized controlled trial, which found no change in periacetabular bone loss between a 3D porous none-hydroxyapatite coated titanium cup and a standard porous hydroxyapatite coated cup over a two year follow-up period by extending the follow-up duration to ten years post-surgery.
Methods:
This was a single-centre, long-term follow-up study conducted over a ten year period in patients who had previously participated in a randomized controlled trial comparing a 3D porous titanium construct shell (PTC group) with a standard porous hydroxyapatite coated titanium shell (PC-group). The primary outcome measured was the change in bone mineral density (BMD) within four specific periacetabular zones, alongside overall bone loss, which was assessed through BMD in the lumbar spine at two, six and ten years postoperatively. Secondary outcomes included clinical outcome measures.
Results:
In total, 18 in the PTC and 20 in the PC group were analysed for the primary endpoint up to ten years. The mean bone mineral density in zones 1-4 was 3.7% higher in the PTC group than in the PC group at six years postoperatively and 12.0% higher at ten years. Clinical outcomes, and the frequency of adverse events did not differ between the groups.
Conclusions:
The PTC group displayed superior long-term bone preservation compared to the PC group while maintaining similar clinical outcomes up to ten years postoperatively. Although with a small sample size, our findings suggest that porous titanium cups have the potential to minimize BMD loss around the cup which could contribute to improving THA outcomes and implant durability.