Oxalate-derived porous C-doped NiO with amorphous-crystalline heterophase for supercapacitors

Constructing amorphous/crystalline heterophase structure with high porosity is a promising strategy to effectively tailor the physicochemical properties of electrode materials and further improve the electrochemical performance of supercapacitors. Here, the porous C-doped NiO (C-NiO) with amorphous/crystalline heterophase grown on NF was prepared using NF as Ni source via a self-sacrificial template method. Calcining the self-sacrificial NiC₂O₄ template at a suitable temperature (400 °C) was beneficial to the formation of porous heterophase structure with abundant cavities and cracks, resulting in high electrical conductivity and rich ion/electron-transport channels. The density functional theory (DFT) calculations further verified that in-situ C-doping could modulate the electronic structure and enhance the OH^- adsorption capability. The unique porous amorphous/crystalline heterophase structure greatly accelerated electrons/ions transfer and Faradaic reaction kinetic, which effectively improved the charge storage. The C-NiO calcined at 400 °C (C-NiO₍₄₀₀₎) displayed a markedly enhanced specific charge, outstanding rate property and excellent cycling stability. Furthermore, the hybrid supercapacitor assembled by C-NiO₍₄₀₀₎ and active carbon achieved a high energy density of 49.0 Wh kg^-1 at 800 W kg^-1 and excellent cycle stability (90.9 % retention at 5 A/g after 10 000 cycles). This work provided a new strategy for designing amorphous/crystalline heterophase electrode materials in high-performance energy storage.