Acid precipitation-hydrothermal synthesis of needle-like hydroxyapatite for protein adsorption from waste

Shanzhu Jiang1, Zhaobo Wang1, Yangjie Qin1

  • 1Phosphogypsum Utilization R&D Center, Hubei Three Gorges Laboratory, Yichang, People's Republic of China.

Environmental Technology
|September 11, 2024
PubMed

Keywords:
Phosphogypsum (PG)bovine serum albumin (BSA)hydroxyapatite (HAP)lysozyme (LYS)protein adsorption

More Related Videos

Synthesis of Graphene-Hydroxyapatite Nanocomposites for Potential Use in Bone Tissue Engineering07:14

Synthesis of Graphene-Hydroxyapatite Nanocomposites for Potential Use in Bone Tissue Engineering

Published on: July 27, 2022

3.6K
Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent11:14

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

Published on: February 21, 2017

12.4K

Related Concept Videos

Washing, Drying, and Ignition of Precipitates00:52

Washing, Drying, and Ignition of Precipitates

After filtration, the precipitate is washed to remove coprecipitated impurities and any remaining mother liquor. Colloidal precipitates, such as silver chloride, are washed with an electrolyte (such as dilute nitric acid) to prevent the peptization of the precipitate. In the case of slightly soluble precipitates, the wash solution contains a common ion to reduce solubility. Lead sulfate, which is slightly soluble in water, is washed with dilute sulfuric acid. Similarly, wash solutions may be...
887
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
202
Precipitation Processes01:12

Precipitation Processes

The experimental conditions in a gravimetric analysis should be optimized to maximize the particle size and purity of the obtained precipitate. Ideally, the concentration of the precipitating reagent should be low with effective stirring to maintain low relative supersaturation for the growth of large crystals. In homogeneous precipitation, the precipitant is slowly generated by a chemical reaction in the solution to avoid local reagent excesses. For example, urea decomposes gradually to...
434
Precipitation and Co-precipitation01:17

Precipitation and Co-precipitation

Precipitation and coprecipitation methods can be used to separate a mixture of ions in a solution. In qualitative inorganic analysis, ions that form sparingly soluble precipitates with the same reagent are separated based on the differences in solubility products. For example, consider the separation of Cu(II) and Fe(II) ions by precipitation as insoluble sulfides. First, copper(II) sulfide is precipitated by the addition of acidic H2S, where the dissociation of H2S is suppressed. Adding H2S...
1.7K
Colloidal precipitates01:09

Colloidal precipitates

The high insolubility of some precipitates can result in an unfavorable relative supersaturation. This can lead to colloidal particles with a large surface-to-mass ratio, where adsorption is promoted. For instance, in the precipitation of silver chloride, silver ions are adsorbed on the surface of the colloidal particles, forming a primary layer. This layer attracts ions of opposite charge (such as nitrate ions), forming a diffuse secondary layer of adsorbed ions. This electric double layer...
524