Diamond-like carbon (DLC) surface treatment decreases biofilm burden by S. aureus on titanium alloy in vitro- a pilot
Anabelle Visperas1, Kaixi Cui2, Md Masud Alam2
1Cleveland Clinic Adult Reconstruction Research (CCARR), Department of Orthopaedic Surgery, Cleveland Clinic, 9500 Euclid Ave. A40, Cleveland, OH, 44113, USA.
Purpose:
Periprosthetic joint infection is a complication of total joint arthroplasty with treatment costs over $1.6 billion dollars per year in the US with high failure rates. Therefore, generation of coatings that can prevent infection is paramount. Diamond-like carbon (DLC) is an ideal coating for implants as they are wear-resistant, corrosion-resistant, inert, and have a low friction coefficient. The purpose of this study was to test the efficacy of DLC surface treatment in prevention of biofilm on titanium discs infected with Staphylococcus aureus in vitro.
Methods:
Titanium alloy discs (n = 4 non-coated and n = 4 DLC-coated) were infected with 5 × 105 colony-forming units (CFU) of S. aureus for 2 weeks then analysed via crystal violet and scanning electron microscopy (SEM).
Results:
Crystal violet analysis yielded differences in the appearance of biofilm on implant surface where DLC-coated had a clumpier appearance but no difference in biofilm quantification. Interestingly, this clumpy appearance did lead to differences in SEM biofilm coverage where significantly less biofilm coverage was found on DLC-coated discs (81.78% vs. 54.17%, p < 0.003).
Conclusion:
DLC-coated titanium alloy implants may have preventative properties in S. aureus infection. Observing differences in biofilm coverage does warrant additional testing including CFU titration and biofilm kinetics with eventual use in an animal model of periprosthetic joint infection.