Influence of carbon content and irradiation modes on the antibiotic removal from water using VIS-activated...

TiO₂/expanded graphite (TiO₂/EG) composite films were applied to water treatment for sulfadiazine (SDZ) degradation in a continuous flat plate photochemical reactor. The films were synthesized by sol-gel method and deposited on borosilicate glass by airbrush spray coating technique, forming a TiO₂/C heterojunction. Increasing the amount of carbon promoted more efficient photocatalytic removal of SDZ under simulated sunlight, which increased from 9.1% in the absence of carbon to 49.8% for the material containing 7.5% C. From the formation of the TiO₂/C heterojunction, morphological modifications, changes in the electronic structure and reduction of the band gap energy were observed. Type-II heterojunction formation was observed. Foreground and background irradiation modes were investigated, and a possible photocatalytic mechanism was proposed. TiO₂/7.5 %-EG exhibited the best photocatalytic performance, with the possibility of reuse. The films showed good reusability in the SDZ degradation over 4 photocatalytic cycles. The influence of irradiation modes and the role of oxidizing species were discussed. The results showed that TiO₂/EG hybrid films are a promising alternative for practical photocatalytic applications under sunlight.