Enhancing High-Temperature Performance of Flexible Pavement with Plastic-Modified Asphalt

Previous studies indicate that traditional asphalt mixtures lack the ability to withstand the stresses caused by heavy traffic volumes under high temperatures. To enhance the rutting resistance of flexible pavement under high levels of temperature and loading, extensive laboratory experiments were carried out. A 60/70 grade bitumen was used as a neat sample for comparison. The study introduced three distinct polymers, polypropylene (PP), low-density polyethylene (LDPE), and acrylonitrile butadiene styrene (ABS), at varying concentrations by weight into the neat bitumen. Initially, conventional tests were performed to evaluate the conventional properties of both the neat and modified bitumen, while aggregate tests assessed the mechanical properties of the aggregates. Subsequently, a Marshall mix design was performed to determine the optimum bitumen content (OBC) in the asphalt mixture. Finally, wheel-tracking tests were performed under a specific load and temperature to investigate the rutting behavior of the modified asphalt mixtures. The results of this comprehensive study revealed that the modified asphalt mixtures displayed improved resistance to rutting compared to the neat asphalt mixture. Furthermore, it was also observed that the LDPE exhibited a superior performance against rutting, followed by the PP and ABS. At polymer contents of 3%, 5%, and 7%, the LDPE achieved reductions in rut depth of 13%, 24%, and 33%, respectively, outperforming both PP- and ABS-modified asphalt. These findings not only enhance our understanding of asphalt behavior under diverse conditions but also highlight the potential of plastic-modified asphalt as an effective solution for mitigating rutting problems in road pavements. By incorporating plastic modifiers into asphalt mixtures, this approach aligns with the principles of sustainable construction by reducing plastic waste while improving pavement durability and performance.