The Influence of Mixing Speed on the Physicomechanical Parameters of Polyaddition Poly(dimethylsiloxanes) with

Ewelina Chmielnicka1,2, Małgorzata Szymiczek2, Błażej Chmielnicki1

  • 1Łukasiewicz Research Network-Institute of Engineering of Polymer Materials and Dyes, M. Skłodowskiej-Curie St. 55, 87-100 Torun, Poland.

Polymers
|September 14, 2024
PubMed

Keywords:
polyaddition poly(dimethylsiloxane)surface resistivitythermography

More Related Videos

Prescribed 3-D Direct Writing of Suspended Micron/Sub-micron Scale Fiber Structures via a Robotic Dispensing System10:36

Prescribed 3-D Direct Writing of Suspended Micron/Sub-micron Scale Fiber Structures via a Robotic Dispensing System

Published on: June 12, 2015

8.0K
Drawing and Hydrophobicity-patterning Long Polydimethylsiloxane Silicone Filaments07:56

Drawing and Hydrophobicity-patterning Long Polydimethylsiloxane Silicone Filaments

Published on: January 7, 2019

8.9K

Related Concept Videos

Additives and Fillers in Concrete01:29

Additives and Fillers in Concrete

Additives and fillers are integral to enhancing the properties of concrete. Pozzolans and blast-furnace slag are additives or admixtures due to their reactions with calcium hydroxide released during cement hydration. Fillers, which are finely ground and similar in fineness to Portland cement, improve concrete attributes such as workability density, and reduce capillary bleeding or cracking. Some fillers possess hydraulic properties or participate in benign reactions within the cement paste.
The...
92
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
2.2K
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
2.4K