A Template Method Leads to Precisely Synthesize SiO₂@Fe₃O₄ Nanoparticles at the Hundred-Nanometer Scale

Constructing photonic crystals with core-shell structured nanoparticles is an important means for applications such as secure communication, anti-counterfeiting marking, and structural color camouflage. Nonetheless, the precise synthesis technology for core-shell structured nanoparticles at the hundred-nanometer scale faces significant challenges. This paper proposes a controlled synthesis method for core-shell structured nanoparticles using a template method. By using 100 nm diameter silica nanospheres as templates and coating them with a ferroferric oxide shell layer, SiO₂@Fe₃O₄ core-shell structured nanoparticles with regular morphology and good uniformity can be obtained. The study experimentally investigated the effects of feed amount, modifiers, temperature, and feed order on the coating effect, systematically optimizing the preparation process. Centrifugal driving technology was used to achieve structural colors in the visible wavelength range. Additionally, the method successfully created well-defined and uniform core-shell structured nanoparticles using 200 nm diameter silica nanospheres as templates, demonstrating that this controllable synthesis method can effectively produce core-shell structured nanoparticles over a wide range of particle sizes. The template method proposed in this paper can significantly improve morphological regularity and size uniformity while effectively reducing the preparation cost of core-shell structured nanoparticles.