In Situ Analysis of Binder Degradation during Catalyst-Accelerated Stress Test of Polymer Electrolyte Membrane Fuel...

High-oxygen-permeability ionomers (HOPIs) are being actively developed to enhance the performance and durability of high-power polymer electrolyte membrane fuel cells (PEMFCs). While methods for evaluating binder performance are well-established, techniques for assessing binder durability and measuring its degradation in situ during the AST process remain limited. This study examines the distribution of relaxation times (DRT) and Warburg-like response (WLR) methods as in situ analysis techniques during the catalyst-accelerated stress test (AST) process. We conducted catalyst-ASTs (0.6-0.95 V cycling) for 20,000 cycles, monitoring changes using cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and linear sweep voltammetry (LSV). Contrary to expectations, during the catalyst-AST, the ion transport resistance of the binder decreased, indicating no binder degradation. Scanning electron microscopy/energy dispersive spectrometer (SEM/EDS) analysis revealed that the degradation rate of the catalyst and the support was relatively higher than that of the binder, leading to a reduction in catalyst layer thickness and improved binder network formation. By applying the DRT method during the catalyst-AST process, we were able to measure the increase in oxygen reduction reaction (ORR) resistance and the decrease in proton transport resistance in situ. This allowed for the real-time detection of the reduction in catalyst layer thickness and improvements in ionomer networks due to catalyst and support degradation. These findings provide new insights into the complex interplay between catalyst degradation and binder performance, contributing to the development of more durable PEMFC components.