Antibacterial and Anticorrosive Hydrogel Coating Based on Complementary Functions of Sodium Alginate and g-C₃N₄

Graphitic carbon nitride (g-C₃N₄, CN) has emerged as a promising photocatalytic material due to its inherent stability, antibacterial properties, and eco-friendliness. However, its tendency to aggregate and limited dispersion hinder its efficacy in practical antibacterial applications. To address these limitations, this study focuses on developing a composite hydrogel coating, in which sodium alginate (SA) molecules interact electrostatically and through hydrogen bonding to anchor CN, thereby significantly improving its dispersion. The optimal CN loading of 35% results in a hydrogel with a tensile strength of 120 MPa and an antibacterial rate of 99.87% within 6 h. The enhanced mechanical properties are attributed to hydrogen bonding between the -NH2 groups of CN and the -OH groups of SA, while the -OH groups of SA facilitate the attraction of photogenerated holes from CN, promoting carrier transfer and separation, thereby strengthening the antibacterial action. Moreover, the hydrogel coating exhibits excellent antibacterial and corrosion resistance capabilities against Pseudomonas aeruginosa on 316L stainless steel (316L SS), laying the foundation for advanced antimicrobial and anticorrosion hydrogel systems.