Increased hydrophilicity of lignin-derivable vs. bisphenol-based polysulfones for potential water filtration
Jignesh S Mahajan1,2, Hoda Shokrollahzadeh Behbahani3, Matthew D Green3
1Department of Materials Science and Engineering, University of Delaware Newark Delaware 19716 USA lkorley@udel.edu.
Abstract:
The functionality inherent in lignin-derivable aromatics (e.g., polar methoxy groups) can provide a potential opportunity to improve the hydrophilicity of polysulfones (PSfs) without the need for the additional processing steps and harsh reagents/conditions that are typically used in conventional PSf modifications. As determined herein, lignin-derivable PSfs without any post-polymerization modification exhibited higher hydrophilicity than comparable petroleum-based PSfs (commercial/laboratory-synthesized) and also demonstrated similar hydrophilicity to functionalized BPA-PSfs reported in the literature. Importantly, the lignin-derivable PSfs displayed improved thermal properties relative to functionalized BPA-PSfs in the literature, and the thermal properties of these bio-derivable PSfs were close to those of common non-functionalized PSfs. In particular, the glass transition temperature (T g) and degradation temperature of 5% weight loss (T d5%) of lignin-derivable PSfs (T g ∼165-170 °C, T d5% ∼400-425 °C) were significantly higher than those of typical functionalized BPA-PSfs in the literature (T g ∼110-160 °C, T d5% ∼240-260 °C) and close to those of unmodified, commercial/laboratory-synthesized BPA-/bisphenol F-PSfs (T g ∼180-185 °C, T d5% ∼420-510 °C).