Impact of agar-glycerol ratios on the physicochemical properties of biodegradable seaweed films: A compositional...

To develop technology more applicable to industrial settings, this study aimed to produce agar-based bioplastic films using extrusion followed by hot compression. The research examined various amounts of glycerol incorporation as the plasticizer, which also facilitated the flowability of the extrusion process. These variations included agar-glycerol ratios of 75:25, 70:30, 65:35, 60:40, and 55:45 (% w/w). Moreover, the films underwent thorough testing to assess their physical, mechanical, chemical, water sensitivity, surface imaging, and biodegradability properties. The results showed that increasing the amount of glycerol in the agar film matrix generally made the films more sensitive to water, resulting in greater hydrophilicity. This change was primarily owing to the increased presence of hydroxyl groups. It also affected other characteristics, such as enhancing the film's stretchability and thermal stability. Furthermore, a decrease in film density was observed, leading to reduced tensile strength and barrier properties. Moreover, the higher glycerol content improved its surface wettability and the higher agar content accelerated the film's biodegradability rate. Microstructural examination using scanning electron microscopy and chemical analysis (FTIR) revealed a homogeneous mixture of agar and glycerol produced through the extrusion process. These findings demonstrate the potential of extrusion techniques for the large-scale production of agar-based bioplastics.