Simultaneously Enhancing the Efficiency and Stability of Perovskite Solar Cells by Using P3HT/PEDOT:PSS as a Double...

The stability issue of perovskite solar cells (PSCs) has long been of concern to researchers. Poly (3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) is commonly used as a hole transport layer (HTL) in the inverted PSCs to achieve efficient and stable performance. However, PEDOT:PSS can corrode ITO, affecting device efficiency. Moreover, the hydrophilic nature of PEDOT:PSS compromises device stability. In this work, Poly (3-hexylthiophene-2,5-diyl) (P3HT), known for its good hydrophobicity, was used to modify the surface of PEDOT:PSS, reducing its water absorption and thereby enhancing the efficiency and stability of PSCs. The results reveal that incorporating P3HT effectively enhances the hydrophobicity of PEDOT:PSS. Furthermore, it fosters the development of large-grain perovskite film on the PEDOT:PSS/P3HT bilayer. This enhancement leads to a power conversion efficiency (PCE) of 19.78% for PSCs, with an increase by 16% than that of reference cells (17.04% of PCE). Following a duration of 1000 h, the PCE for the device modified with P3HT remains above 90%, while the PCE of the reference device is below 70%. These findings suggest that using P3HT in conjunction with PEDOT:PSS as a bilayer HTL can concurrently and proficiently improve the efficiency and stability of PSCs.