Effect of sintering cycle on the strength and translucency of multilayered zirconia

A newly introduced sintering protocol promises to offer higher translucency while not significantly compromising the flexural strength of the material. However, the effect of the novel sintering protocol has not been thoroughly validated. The purpose of this study was to measure and compare the effect of two sintering protocols on the translucency and flexural strength of two multilayered zirconia materials.

Two types of multilayered zirconia materials (ZirCAD Prime and Prime esthetic) were selected. Presintered disk specimens were obtained from Translucent, Gradient, and Dentin layers (n = 20). The disks were allocated to 2 groups: standard sintering protocol (peak temperature 1500°C) and high translucency sintering protocol (peak temperature 1600°C). After the sintering process, 10 specimens from each group were randomly selected. The optical values (L^*, a^*, b^*) were measured and used to assess translucency using the relative translucency parameter (RTP₀₀) and translucency differences (ΔRTP₀₀). Then, all 20 specimens were tested for biaxial flexural strength. The outcomes were analyzed. The analysis of variance is used to analyze any significant effects on translucency and flexural strength. Then, any significant difference in the translucency and flexural strength between all pairs of materials was analyzed using Bonferroni-corrected Student's t-test (α = 0.05).

The high translucency sintering protocol significantly decreased biaxial strength in the Prime translucent and dentine layer, Prime esthetic translucent, and gradient layer. RTP₀₀ was significantly reduced in the Prime gradient and Prime esthetic gradient layer when sintered with a high translucency protocol. The lowest ΔRTP₀₀ was observed in the Prime dentine layer, while the highest ΔRTP₀₀ was observed in the Prime esthetic dentin layer.

High translucency protocol significantly lowers the biaxial flexural strength of both multilayered materials, but the alteration in translucency is within clinically acceptable thresholds (TAT₀₀ = 2.62).