Exploring strategies for valorizing wood processing waste: advancing sustainable, fully lignocellulosic biocomposites

This study presents the design and synthesis of bio-composites exhibiting high properties, wherein both the matrix and filler originate from wood biomass. Notably, no additional hardener compounds or treatments/modifications of the lignocellulosic filler were employed. Thermosetting materials were developed by homopolymerizing a bio-based aromatic epoxy monomer, the resorcinol diglycidyl ether (RDGE), with different percentages, from 1 wt% to 30 wt% of natural wood processing side-product, such as spruce bark powder (SB), which was used as such without additional treatments and modifications. The DSC analyses revealed enhanced reactivities with the bio-filler content, resulting in a reduced reaction temperature range and maximum reaction temperature. These findings provide evidence of the chemical interaction between the functional groups from spruce bark and the epoxides groups. The obtained fully based lignocellulosic materials show high E' values from 2.4 GPa to 2.5-3.5 GPa (glassy state) and from 64 MPa to 99-156 MPa in the rubbery region. The damping factor of the bio-composites with 1-10 wt% SB have shown an increase of the α transition temperature from 92 °C to 94-97 °C. The excellent filler/matrix interface and optimal adhesion between them were confirmed by SEM analysis.