Investigation of Microstructure and Interfacial Reactions of Diffusion Bonding of Ni-Ti6Al4V Materials Joined by...

Due to its super plasticity, low weight, and high mechanical resistance properties, generally, Ti6Al4V is used for aeronautical applications. However, it has low resistance to plastic shearing. In addition, it has poor wear resistance. For these reasons, a lot of techniques have been developed to improve its wear resistance. Investigations of microstructure and interfacial reactions of diffusion bonding of Ni and Ti6Al4V materials have been performed experimentally. Ni samples were prepared with 50 ± 5 µm Ni powders in cylindrical shape. For diffusion bonding, Ag foil was used for improving the interlayer and connection quality. Nickel and its alloys can be joined by using some different processes, and the use of an interlayer can further facilitate the joining process and improve the joint quality. The experiments were carried out under the protected atmosphere. Argon gas was used for protection. The experiments were performed under 5 MPa pressure for 60 min duration at 850 °C, 900 °C, and 950 °C thermal conditions. Investigations of metallurgical structure occurring in the interface areas were examined by optic analysis of EDS, SEM, and X-ray. The strength of the joints was tested by lap-shear tests. From observations, the best quality of the coalescence at interfaces was indicated at elevated temperatures.